The results of direct synthesis of boron nitride from boron powders of mean sizes of 0.05, 0.20, and 2.00 μm in nitrogen flow with impurity of H2O in a xenon high-flux optical furnace are presented. Formation of equiaxed, plate-like powders and film-like structures of different sizes was observed.