In the Current work, hybrid composites were prepared by reinforcing nanoparticles into the aluminum alloys (Al 6068 and Al 7075). The Al 6068 and Al 7075 aluminum alloys are reinforced with TiO2 and BN by a stir casting process. The wear behavior and mechanical properties were investigated by performing hardness test and tensile test and compressive test and wear test was conducted under the dry sliding conditions. And performed the microstructural study to know the bond formed between the alloy and reinforcements. The samples are prepared as per ASME standards, and stirring speed (650 rpm), stirring time(15 min), % weight of reinforcement (3%), and stirring temperature (7500 C) is considered as process parameters to fabricate the samples to perform mechanically and wear properties. The samples are fabricated by the combination Al 6068+TiO2, Al 6068+BN, Al 6068+TiO2+BN, Al 7075+TiO2, Al 7075+BN, and Al 7075+TiO2+BN. And the mechanical test was performed and studied the results obtained, and also the wear behavior of the hybrid composite was recorded and finally the analyzed the bonding between alloy and reinforcements of the composite materials by the SEM images.